BITUMEN COAT/FINISH

SOLVENT THINNED HIGH BUILD BITUMEN BB58
bb58-bitumen

A solvent thinned high build Bitumen coating and finish paint, for walls, structural steel, galvanised substrates, concrete and brick.

  • Tough hard-wearing film.
  • Excellent water resistance.
  • Suitable for water immersion (not drinking water or fish ponds).
  • Confirms to BS 3416 and BS6949, Type 1 Class A.

SUITABLE FOR:

Steel and non-ferrous metals properly prepared and primed where necessary. Concrete and brick free of contamination, dust and efflorescence, properly prepared.

APPLICATION:
Brush, Roller & Spray

SHEEN LEVEL:
Gloss

COVERAGE:
16m2 per Litre

TOUCH DRY:
4 Hours

RECOAT:
16 Hrs Min.

AVAILABILITY:
5 Litre

POT LIFE:
N/A

ADDITIONAL INFO:
 Thinner: TW35

Self prime. New Galvanised – degreased & TM38 to be used

*At 50 microns DFT (loss factors will apply in practice)

SUITABLE FOR:

Steel and non-ferrous metals properly prepared and primed where necessary. Concrete and brick free of contamination, dust and efflorescence, properly prepared.

APPLICATION:
Brush, Roller & Spray

SHEEN LEVEL:
Gloss

COVERAGE:
16m2 per Litre

TOUCH DRY:
4 Hours

RECOAT:
16 Hrs Min.

AVAILABILITY:
5 Litre

POT LIFE:
N/A

ADDITIONAL INFO:
 Thinner: TW35

Self prime. New Galvanised – degreased & TM38 to be used

*At 50 microns DFT (loss factors will apply in practice)

Correct preparation is vital to ensure you obtain the full benefit from Bradite Metal Paints.

New and unpainted steel

  • High pressure water cleaning to remove all loose salts and other contaminants.
  • Degrease using BRADITE TD39, with scrubbing plus high pressure water cleaning to remove any oil contamination not removed by high pressure cleaning alone, rinse with clean water and allow to dry.
  • Mechanically or manually prepared steel to a clean metallic finish, SIS-St 3 minimum.
  • Substrate to be dry, clean and free of contamination and dust free prior to coating.

Existing coatings

  • Jet wash to remove all loose and flaking paint, salts and other contaminants.
  • Degrease using Bradite TD39 diluted with up to 9 parts of warm water and scrubbing to remove any oil contamination not removed with jet washing alone. Rinse with clean water and allow to dry.
  • Existing coatings should be well adhered with all edges tight and well feathered.
  • Bare or rusted steel should be manually or mechanically abraded to a clean metallic finish (SIS-St 3).
  • Substrate should be clean, dust free and dry before application.
  • Spot prime with correct primer.
  • Galvanised steel, aluminium and other non-ferrous metals should be roughened or lightly abraded.
  • New bright galvanised steel should be degreased and treated with Bradite TM38 pre-treatment for galvanised steel.
ALTERNATIVE PRODUCTS

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy